| 布氏硬度 HB | 洛氏硬度 | 维氏 نعم HV | 布氏硬度 HB | 洛氏硬度 | 维氏硬度 HV | ||
| هيئة تنظيم الموارد البشرية | هيئة حقوق الإنسان | هيئة تنظيم الموارد البشرية | هيئة حقوق الإنسان | ||||
| 86.6 | 70.0 | 1037 | 78.5 | 55.0 | 599 | ||
| 86.3 | 69.5 | 1017 | 78.2 | 54.5 | 589 | ||
| 86.1 | 69.0 | 997 | 77.9 | 54.0 | 579 | ||
| 85.8 | 68.5 | 978 | 77.7 | 53.5 | 570 | ||
| 85.5 | 68.0 | 959 | 77.4 | 53.0 | 561 | ||
| 85.2 | 67.5 | 941 | 77.1 | 52.5 | 551 | ||
| 85.0 | 67.0 | 923 | 76.9 | 52.0 | 543 | ||
| 84.7 | 66.5 | 906 | 76.6 | 51.5 | 534 | ||
| 84.4 | 66.0 | 889 | 501 | 76.3 | 51.0 | 525 | |
| 84.1 | 65.5 | 872 | 494 | 76.1 | 50.5 | 517 | |
| 83.9 | 65.0 | 856 | 488 | 75.8 | 50.0 | 509 | |
| 83.6 | 64.5 | 840 | 481 | 75.5 | 49.5 | 501 | |
| 83.3 | 64.0 | 825 | 474 | 75.3 | 49.0 | 493 | |
| 83.1 | 63.5 | 810 | 468 | 75.0 | 48.5 | 485 | |
| 82.8 | 63.0 | 795 | 461 | 74.7 | 48.0 | 478 | |
| 82.5 | 62.5 | 780 | 455 | 74.5 | 47.5 | 470 | |
| 82.2 | 62.0 | 766 | 449 | 74.2 | 47.0 | 463 | |
| 82.0 | 61.5 | 752 | 442 | 73.9 | 46.5 | 456 | |
| 81.7 | 61.0 | 739 | 436 | 73.7 | 46.0 | 449 | |
| 81.4 | 60.5 | 726 | 430 | 73.4 | 45.5 | 443 | |
| 81.2 | 60.0 | 713 | 424 | 73.2 | 45.0 | 436 | |
| 80.9 | 59.5 | 700 | 418 | 72.9 | 44.5 | 429 | |
| 80.6 | 59.0 | 688 | 413 | 72.6 | 44.0 | 423 | |
| 80.3 | 58.5 | 676 | 407 | 72.4 | 43.5 | 417 | |
| 80.1 | 58.0 | 664 | 401 | 72.1 | 43.0 | 411 | |
| 79.8 | 57.5 | 653 | 396 | 71.8 | 42.5 | 405 | |
| 79.5 | 57.0 | 642 | 391 | 71.6 | 42.0 | 399 | |
| 79.3 | 56.5 | 631 | 385 | 71.3 | 41.5 | 393 | |
| 79.0 | 56.0 | 620 | 380 | 71.1 | 41.0 | 388 | |
| 78.7 | 55.5 | 609 | 375 | 70.8 | 40.5 | 382 | |
جدول تحويل قيم صلابة المواد المعدنية الحديدية
| 布氏硬度 HB | 洛氏硬度 | 维氏硬度 HV | 布氏硬度 HB | 洛氏硬度 | 维氏硬度 HV | ||
| هيئة تنظيم الموارد البشرية | هيئة حقوق الإنسان | هيئة تنظيم الموارد البشرية | هيئة حقوق الإنسان | ||||
| 370 | 70.5 | 40.0 | 377 | 269 | 28.0 | 274 | |
| 365 | 70.3 | 39.5 | 372 | 266 | 27.5 | 271 | |
| 360 | 70.0 | 39.0 | 367 | 263 | 27.0 | 268 | |
| 355 | 38.5 | 362 | 260 | 26.5 | 264 | ||
| 350 | 38.0 | 351 | 257 | 26.0 | 261 | ||
| 345 | 37.5 | 352 | 254 | 25.5 | 258 | ||
| 341 | 37.0 | 347 | 251 | 25.0 | 255 | ||
| 336 | 36.5 | 342 | 248 | 24.5 | 252 | ||
| 332 | 36.0 | 338 | 245 | 24.0 | 249 | ||
| 327 | 35.5 | 333 | 242 | 23.5 | 246 | ||
| 323 | 35.0 | 329 | 240 | 23.0 | 243 | ||
| 318 | 34.5 | 324 | 237 | 22.5 | 240 | ||
| 314 | 34.0 | 320 | 234 | 22.0 | 237 | ||
| 310 | 33.5 | 316 | 232 | 21.5 | 234 | ||
| 306 | 33.0 | 312 | 229 | 21.0 | 231 | ||
| 302 | 32.5 | 308 | 227 | 20.5 | 229 | ||
| 298 | 32.0 | 304 | 225 | 20.0 | 226 | ||
| 294 | 31.5 | 300 | 222 | 19.5 | 223 | ||
| 291 | 31.0 | 296 | 220 | 19.0 | 221 | ||
| 287 | 30.5 | 292 | 218 | 18.5 | 218 | ||
| 283 | 30.0 | 289 | 216 | 18.0 | 216 | ||
| 280 | 29.5 | 285 | 214 | 17.5 | 214 | ||
| 276 | 29.0 | 281 | 211 | 17.0 | 211 | ||
| 273 | 28.5 | 278 | |||||
ملحوظة:
1. صلابة برينل: تُستخدم بشكل أساسي لقياس صلابة المسبوكات، والمطروقات، وأجزاء المعادن غير الحديدية، والسبائك المدرفلة على الساخن، والأجزاء المُلدّنة. نطاق القياس ≥ 450 HB.
2. صلابة روكويل: تُستخدم صلابة روكويل (HRA) بشكل أساسي لقياس صلابة سطح المواد والأسطح التي تزيد صلابتها عن 67 HRC، مثل كربيد التنجستن والفولاذ المُنترد، وما إلى ذلك. يتراوح نطاق القياس بين 70 و70 HRC. أما صلابة روكويل (HRC) فتُستخدم بشكل أساسي لقياس صلابة أجزاء الفولاذ (مثل الفولاذ الكربوني، وفولاذ الأدوات، والفولاذ السبائكي، وما إلى ذلك) بعد التبريد السريع أو التطبيع. يتراوح نطاق القياس بين 20 و67 HRC.
3. صلابة فيكرز: تستخدم لقياس صلابة الأجزاء الرقيقة وأجزاء الصفائح الفولاذية، ويمكن استخدامها أيضًا لقياس صلابة الأجزاء التي تم تصلب سطحها مثل الكربنة والسيانيد والنتردة.